聚苯醚PPO NORYL HB1525(图)
供应商:东莞市塑大塑胶原料有限公司[查看公司详情]
所在地:广东 东莞市 樟木头镇塑胶市场一期Z栋09A号
价格:30.20元
经营模式:经销批发
联系人:秦再娥
产品简介
Specific Gravity | 1.06 | 1.06 | ASTM D 792 |
Density | 1.06 | 0.0383 lb/in3 | ISO 1183 |
Moisture Absorption at Equilibrium | 0.0600 % | 0.0600 % | 23°C/50% RH; ISO 62 |
Water Absorption at Saturation | 0.230 % | 0.230 % | ISO 62 |
Linear Mold Shrinkage, Flow | 0.00500 - 0.00700
cm/cm @Thickness 3.20 mm | 0.00500 - 0.00700 in/in @Thickness 0.126 in | SABIC Method |
Melt Flow | 20.0 g/10 min @Load 3.80 kg, Temperature 280 °C | 20.0 g/10 min @Load 8.38 lb, Temperature 536 °F | Melt Volume Rate (cm^3/10 min); ISO 1133 |
21.0 g/10 min @Load 3.80 kg, Temperature 280 °C | 21.0 g/10 min @Load 8.38 lb, Temperature 536 °F | ASTM D 1238 | |
Hardness, Rockwell R | 106 | 106 | ISO 2039-2 |
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527 |
39.0 MPa | 5660 psi | Type I, 50 mm/min; ASTM D 638 | |
Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D 638 | |
Elongation at Break | 40.0 % | 40.0 % | 50 mm/min; ISO 527 |
40.0 % | 40.0 % | Type I, 50 mm/min; ASTM D 638 | |
Elongation at Yield | 2.30 % | 2.30 % | 50 mm/min; ISO 527 |
2.60 % | 2.60 % | Type I, 50 mm/min; ASTM D 638 | |
Tensile Modulus | 1.85 GPa | 268 ksi | 1 mm/min; ISO 527 |
1.90 GPa | 276 ksi | 5 mm/min; ASTM D 638 | |
Flexural Modulus | 1.85 GPa | 268 ksi | 2 mm/min; ISO 178 |
2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
Flexural Yield Strength | 52.0 MPa | 7540 psi | 2 mm/min; ISO 178 |
60.0 MPa | 8700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
Charpy Impact, Notched | 0.600 J/cm2 @Thickness 4.00 mm, Temperature -30.0 °C | 2.86 ft-lb/in2 @Thickness 0.157 in, Temperature -22.0 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
1.10 J/cm2 @Thickness 4.00 mm, Temperature 23.0 °C | 5.24
ft-lb/in2 @Thickness 0.157 in, Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
Impact Test | 27.0 J | 19.9 ft-lb | Instrumented Impact Total Energy; ASTM D 3763 |
Taber Abrasion, mg/1000 Cycles | 90.0 | 90.0 | CS-17, 1 kg; SABIC Method |
Izod Impact, Notched | 1.00 J/cm @Temperature -30.0 °C | 1.87 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
1.50 J/cm @Temperature 23.0 °C | 2.81
ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
Izod Impact, Notched (ISO) | 7.00 kJ/m2 @Thickness 4.00 mm, Temperature -30.0 °C |
3.33 ft-lb/in2 @Thickness 0.157 in, Temperature -22.0 °F | 80*10*4; ISO 180/1A |
9.00 kJ/m2 @Thickness 4.00 mm, Temperature 23.0 °C | 4.28
ft-lb/in2 @Thickness 0.157 in, Temperature 73.4 °F | 80*10*4; ISO 180/1A |
AES/韩国锦湖/HW601HI高透明高抗冲抗紫外线耐候挤出片材原料
POM日本旭化成LD755共聚物 高流量 高刚度 翘曲变形 润滑
诚信经营CPVC法国EC950挤出高强度高韧性双壁波纹管原料
PP-R 台湾福聚7011 耐温耐老化管材PPR原料高抗冲PP-R原料
诚信会员POM日本旭化成4520注塑高刚性高流动高韧性汽车部件原料
用于车轮,滚轴,紧固件,汽车领域的应用POM 8005日本宝理
高耐磨聚甲醛泰科纳Hostaform EC140XF高强度 齿轮专用料
POM/德国巴斯夫/N2200G63用于耐腐蚀性的材料制作 高刚性 高韧性
高强度POM日本旭化成Tenac-C TFC64用于注塑高耐磨导电部件原料
泰科纳Hostaform C9021 注塑高耐磨高刚性手动喷雾器部件原料
POM日本旭化成Tenac-C加碳纤增强CF454用于齿轮齿轮联轴节
推荐产品PC/ABS韩国三星HE-1071高光泽注塑变压器外壳 高韧性
玻璃纤维增强阻燃性能 韩国LG PBT LW5303F 食品级
注塑 玻纤增强级 PBT HR5315HF BK503 美国杜邦 高韧性
CPVC/法国阿科玛/8067 挤出耐高温 耐寒 耐压管材原料
现货供应 耐老化耐腐蚀管材原料PP-R 燕山石化 B4240耐压
高耐磨聚甲醛泰科纳Hostaform C9021FCT1 冲击强度佳